Rare-earth magnet

Article Id: WHEBN0002282444
Reproduction Date:

Title: Rare-earth magnet  
Author: World Heritage Encyclopedia
Language: English
Subject: Neodymium magnet, Rare earth element, Magnetism, Rare earth, Aviation in the digital age
Collection: Ferromagnetic Materials, Loudspeakers, Magnetic Levitation, Types of Magnets
Publisher: World Heritage Encyclopedia
Publication
Date:
 

Rare-earth magnet

Ferrofluid on glass, with a rare-earth magnet underneath.

Rare-earth magnets are strong permanent magnets made from alloys of rare earth elements. Developed in the 1970s and '80s, rare-earth magnets are the strongest type of permanent magnets made, producing significantly stronger magnetic fields than other types such as ferrite or alnico magnets. The magnetic field typically produced by rare-earth magnets can be in excess of 1.4 teslas, whereas ferrite or ceramic magnets typically exhibit fields of 0.5 to 1 tesla. There are two types: neodymium magnets and samarium-cobalt magnets. Rare earth magnets are extremely brittle and also vulnerable to corrosion, so they are usually plated or coated to protect them from breaking, chipping, or crumbling into powder.

The term "rare earth" can be misleading as these metals are not particularly rare or precious;[1][2] they are about as abundant as tin or lead.[3] The development of rare earth magnets began around 1966, when K. J. Strnat and G. Hoffer of the US Air Force Materials Laboratory discovered that an alloy of yttrium and cobalt, YCo5, had by far the largest magnetic anisotropy constant of any material then known.[4][5]

Contents

  • Explanation of strength 1
  • Magnetic properties 2
  • Types 3
    • Samarium-cobalt 3.1
    • Neodymium 3.2
  • Hazards 4
  • Applications 5
    • Common applications 5.1
    • Other applications 5.2
  • Rare-earth-free permanent magnets 6
  • References 7
  • Further reading 8
  • External links 9

Explanation of strength

The rare earth (lanthanide) elements are metals that are ferromagnetic, meaning that like iron they can be permanently magnetized, but their Curie temperatures are below room temperature, so in pure form their magnetism only appears at low temperatures. However, they form compounds with the transition metals such as iron, nickel, and cobalt, and some of these have Curie temperatures well above room temperature. Rare earth magnets are made from these compounds.

The advantage of the rare earth compounds over other magnets is that their crystalline structures have very high magnetic anisotropy. This means that a crystal of the material is easy to magnetize in one particular direction, but resists being magnetized in any other direction.

Atoms of rare earth elements can retain high magnetic moments in the solid state. This is a consequence of incomplete filling of the f-shell, which can contain up to 7 unpaired electrons with aligned spins. Electrons in such orbitals are strongly localized and therefore easily retain their magnetic moments and function as paramagnetic centers. Magnetic moments in other orbitals are often lost due to the strong overlap with their neighboring electrons; for example, electrons participating in covalent bonds form pairs with zero net spin.

High magnetic moments at the atomic level in combination with a stable alignment (high anisotropy) of those atoms results in a high magnetic field strength.

Magnetic properties

Some important properties used to compare permanent magnets are: remanence (Br), which measures the strength of the magnetic field; coercivity (Hci), the material's resistance to becoming demagnetized; energy product (BHmax), the density of magnetic energy; and Curie temperature (Tc), the temperature at which the material loses its magnetism. Rare earth magnets have higher remanence, much higher coercivity and energy product, but (for neodymium) lower Curie temperature than other types. The table below compares the magnetic performance of the two types of rare earth magnet, neodymium (Nd2Fe14B) and samarium-cobalt (SmCo5), with other types of permanent magnets.

Magnet Br (T) Hci (kA/m) (BH)max (kJ/m3) Tc (°C)
Nd2Fe14B (sintered) 1.0–1.4 750–2000 200–440 310–400
Nd2Fe14B (bonded) 0.6–0.7 600–1200 60–100 310–400
SmCo5 (sintered) 0.8–1.1 600–2000 120–200 720
Sm(Co,Fe,Cu,Zr)7 (sintered) 0.9–1.15 450–1300 150–240 800
Alnico (sintered) 0.6–1.4 275 10–88 700–860
Sr-ferrite (sintered) 0.2–0.4 100–300 10–40 450

Types

Samarium-cobalt

Samarium-cobalt magnets (chemical formula: SmCo5), the first family of rare earth magnets invented, are less used than neodymium magnets because of their higher cost and weaker magnetic field strength. However, samarium-cobalt has a higher Curie temperature, creating a niche for these magnets in applications where high field strength is needed at high operating temperatures. They are highly resistant to oxidation, but sintered samarium-cobalt magnets are brittle and prone to chipping and cracking, and may fracture when subjected to thermal shock.

Neodymium

Neodymium magnet with nickel plate mostly removed

Neodymium magnets, invented in the 1980s, are the strongest and most affordable type of rare-earth magnet. They are made of an alloy of neodymium, iron and boron (Nd2Fe14B), sometimes abbreviated as NIB. Neodymium magnets are used in numerous applications requiring strong, compact permanent magnets, such as electric motors for cordless tools, hard drives, magnetic holddowns and jewelry clasps. They have the highest magnetic field strength and have a higher coercivity (which makes them magnetically stable), but they have a lower Curie temperature and are more vulnerable to oxidation than samarium-cobalt magnets. Corrosion can cause unprotected magnets to spall off a surface layer, or to crumble into a powder. Use of protective surface treatments such as gold, nickel, zinc and tin plating and epoxy resin coating can provide corrosion protection.

Originally, the high cost of these magnets limited their use to applications requiring compactness together with high field strength. Both the raw materials and the patent licenses were expensive. Beginning in the 1990s, NIB magnets have become steadily less expensive, and the low cost has inspired new uses such as magnetic construction toys.

Hazards

The greater force exerted by rare earth magnets creates hazards that are not seen with other types of magnet. Magnets larger than a few centimeters are strong enough to cause injuries to body parts pinched between two magnets, or a magnet and a metal surface, even causing broken bones.[6] Magnets allowed to get too near each other can strike each other with enough force to chip and shatter the brittle material, and the flying chips can cause injuries. There have even been cases where young children who have swallowed several magnets have had a fold of the digestive tract pinched between the magnets, causing injury and in one case intestinal perforations, sepsis and death.[7]

Applications

Since their prices became competitive in the 1990s, neodymium magnets have been replacing Alnico and ferrite magnets in the many applications in modern technology requiring powerful magnets. Their greater strength allows smaller and lighter magnets to be used for a given application.

Common applications

Neodymium Magnet Balls

Common applications of rare-earth magnets include:

Other applications

Other applications of rare-earth magnets include:

Rare-earth-free permanent magnets

The United States Department of Energy has identified a need to find substitutes for rare earth metals in permanent magnet technology, and has begun funding such research. The Advanced Research Projects Agency-Energy (ARPA-E) has sponsored a Rare Earth Alternatives in Critical Technologies (REACT) program, to develop alternative materials. In 2011, ARPA-E awarded 31.6 million dollars to fund Rare-Earth Substitute projects.[8]

References

  1. ^ McCaig, Malcolm (1977). Permanent Magnets in Theory and Practice. USA: Wiley. p. 123.  
  2. ^ Sigel, Astrid; Helmut Sigel (2003). The lanthanides and their interrelations with biosystems. USA: CRC Press. pp. v.  
  3. ^ Bobber, R. J. (1981). "New Types of Transducers". Underwater Acoustics and Signal Processing. p. 243.  
  4. ^ Cullity, B. D.; Graham, C. D. (2008). Introduction to Magnetic Materials. Wiley-IEEE. p. 489.  
  5. ^ Lovelace, Alan M. (March–April 1971). "More Mileage Than Programmed From Military R&D". Air University Review (US Air Force) 22 (3): 14–23. Retrieved July 4, 2012. 
  6. ^ Swain, Frank (March 6, 2009). "How to remove a finger with two super magnets". The Sciencepunk Blog. Seed Media Group LLC. Retrieved 2009-06-28. 
  7. ^ "Magnet Safety Alert" (PDF). U.S. Consumer Product Safety Commission. Retrieved 20 July 2014. 
  8. ^ "Research Funding for Rare Earth Free Permanent Magnets". ARPA-E. Retrieved 23 April 2013. 

Further reading

  • Edward P. Furlani, "Permanent Magnet and Electromechanical Devices: Materials, Analysis and Applications", Academic Press Series in Electromagnetism (2001). ISBN 0-12-269951-3.
  • Peter Campbell, "Permanent Magnet Materials and their Application" (Cambridge Studies in Magnetism)(1996). ISBN 978-0-521-56688-9.
  • Brown, D.N.; B. Smith; B.M. Ma; P. Campbell (2004). "The Dependence of Magnetic Properties and Hot Workability of Rare Earth-Iron-Boride Magnets Upon Composition" (PDF). IEEE Transactions on Magnetics 40 (4): 2895–2897.  

External links

  • MMPA 0100-00, Standard Specifications for Permanent Magnet Materials
  • Edwards, Lin (22 March 2010). "Iron-nitrogen compound forms strongest magnet known".  
This article was sourced from Creative Commons Attribution-ShareAlike License; additional terms may apply. World Heritage Encyclopedia content is assembled from numerous content providers, Open Access Publishing, and in compliance with The Fair Access to Science and Technology Research Act (FASTR), Wikimedia Foundation, Inc., Public Library of Science, The Encyclopedia of Life, Open Book Publishers (OBP), PubMed, U.S. National Library of Medicine, National Center for Biotechnology Information, U.S. National Library of Medicine, National Institutes of Health (NIH), U.S. Department of Health & Human Services, and USA.gov, which sources content from all federal, state, local, tribal, and territorial government publication portals (.gov, .mil, .edu). Funding for USA.gov and content contributors is made possible from the U.S. Congress, E-Government Act of 2002.
 
Crowd sourced content that is contributed to World Heritage Encyclopedia is peer reviewed and edited by our editorial staff to ensure quality scholarly research articles.
 
By using this site, you agree to the Terms of Use and Privacy Policy. World Heritage Encyclopedia™ is a registered trademark of the World Public Library Association, a non-profit organization.
 



Copyright © World Library Foundation. All rights reserved. eBooks from Hawaii eBook Library are sponsored by the World Library Foundation,
a 501c(4) Member's Support Non-Profit Organization, and is NOT affiliated with any governmental agency or department.